Adsorptive removal of atmospheric pollutants over Pyropia tenera chars

  • cc icon
  • ABSTRACT

    As a replacement for activated carbon, biochar was synthesized and used for the adsorptive removal of formaldehyde and nitrogen oxide. Biochar was produced from the fast pyrolysis of the red marine macro alga, Pyropia tenera. The P. tenera char was then activated with steam, ammonia and KOH to alter its characteristics. The adsorption of formaldehyde, which is one of the main indoor air pollutants, onto the seaweed char was performed using 1-ppm formaldehyde and the char was activated using a range of methods. The char activated with both the KOH and ammonia treatments showed the highest adsorptive removal efficiency, followed by KOH-treated char, ammonia-treated char, steam-treated char, and non-activated char. The removal of 1000-ppm NO over untreated char, KOH-treated char, and activated carbon was also tested. While the untreated char exhibited little activity, the KOH-treated char removed 80% of the NO at 50℃, which was an even higher NO removal efficiency than that achieved by activated carbon.


  • KEYWORD

    Pyropia tenera char , activation , adsorption , formaldehyde removal , NO removal

  • 1. Introduction

    Rapid urbanization has caused a number of environmental problems, including heavy metal-containing wastewater, air pollutants from vehicles and factories, and global warming due to the increasing fossil fuel consumption; which increasingly threaten the quality of human life [1-8]. In particular, indoor air pollution, which is known to cause “sick building syndrome,” has attracted significant attention because the time urban residents spend indoors has become an increasing portion of their total activities. Construction materials, interior pieces and wallpaper, and furniture used during the construction of houses and buildings, contain a range of volatile organic compounds, including benzene, toluene, and formaldehyde. In addition, other air pollutants, such as nitrogen oxide, carbon monoxide, and asbestos, are also emitted indoors. Exposure to these pollutants in closed spaces can cause headache, dyspnea, atopic dermatitis, urticaria, heart disease, and cancer [9-11].

    Formaldehyde is a representative indoor air pollutant among those responsible for sick building syndrome. Efforts have been made to remove formaldehyde effectively using photocatalytic oxidation [12], catalytic oxidation [13], and biodegradation [14]. Nitrogen oxides are not only indoor air pollutants, but are also the main industrial gaseous wastes emitted from coal combustion processes as well as urban air pollutants emitted from vehicles. The most popular technology for removing nitrogen oxides is selective catalytic reduction [15]. This method, however, cannot be used at room temperature and consumes a large amount of energy. This is why there is still demand for a simpler, more effective, and more economical pollutant removal technology.

    Activated carbon is used widely for the adsorption of noxious gases and heavy metals, as well as for wastewater treatment because of its large adsorption capacity, large surface area, and high porosity [16-25]. On the other hand, the price of commercial activated carbon produced from bituminous coal, coconut shell, wood, or peat is relatively high because of the costly raw materials and expensive activation process [26].

    One of the most important global problems is climate change due to global warming. The application of biomass-derived char as an adsorbent is beneficial not only to the removal of pollutants but also to the reduction of carbon emissions. In particular, use of the byproduct biochar (obtained from fast pyrolysis of biomass aimed at the production of bio-oil) would provide an additional economic advantage [27-39].

    Biochar is obtained from the pyrolysis of a wide range of biomass materials, such as woody materials and agricultural wastes (olive husk, corncob, tea waste, green waste, etc.) [30,40-44]. Having a microporous structure and high C content, biochar can be used in a range of applications [45]. On the other hand, it has an important drawback: its specific surface area, and therefore its adsorption capacity, is smaller than that of activated carbon. Various activation treatment methods have been proposed to enhance the adsorption capacity of biochar [16,46].

    There are approximately 10,000 different species of seaweeds (marine macroalgae), which is more than the number of all land species providing useful biomass. Seaweeds are abundant in coastal regions worldwide. Their life cycle is short; hence the rate of reproduction is high. They are inexpensive and easy to handle. The advantages of seaweeds make them potentially important energy resources [47,48]. Furthermore, they have high selectivity toward the removal of various heavy metal ions, such as gold, cadmium, copper, and zinc (they have exceptional metal binding capacity), making them potential biosorbent materials [49,50]. Seaweed-derived biochar has recently been used for the removal of copper ions in wastewater [46,47,51-53]. To the best of the authors’ knowledge, however, seaweed biochar has never been used for the removal of air pollutants, such as formaldehyde and nitrogen oxide.

    In this study, biochar produced from the fast pyrolysis of a representative seaweed species, Pyropia tenera (Kjellman) (called Porphyra tenera until 2011) was applied to the removal of low-concentrations (1 ppm) of formaldehyde and high-concentrations (1000 ppm) of nitrogen oxide. The characteristics of the char were altered by various activation processes using steam, KOH, and ammonia to improve the adsorption performance [52-55].

    2. Experimental

       2.1. Preparation of samples

    P. tenera was collected from Amtae Island, Shinan, Jeonnam, Korea. The dried seaweed was sieved to leave 75–106 μm particles. The char was produced from the fast pyrolysis of these particles for 1 h at 500℃, under nitrogen flowing at 50 mL/min. The char produced in this way is referred to in this paper as PC, and Fig. 1 shows a schematic diagram of the fast pyrolysis apparatus used to produce PC.

    The char produced from fast pyrolysis was activated with steam, KOH, and ammonia to improve its adsorption characteristics. For steam activation, a gas mixture of 80% N2 and 20% H2O was put through a reactor containing PC at the rate of 50 mL/min. The reactor temperature was increased at 5℃/min to 500℃, and then maintained at that temperature for 1 h. This steam-activated char is referred to in this paper as PCW.

    For KOH activation, a mixture of KOH and char (mass ratio of 1:1) was dried on a hot plate; then dried further in a 110℃ oven for 24 h. The dried char sample was pulverized, placed into a reactor, and calcined for 1 h at 700℃ under flowing nitrogen (50 mL/min). After washing out the residual K+ ions with distilled water, the char sample was neutralized using a 5 M HCl solution and dried. The char activated this way is referred to in this paper as PCK.

    Ammonia activation began by treating PC in a reactor for 2 h with ammonia gas (50 mL/min) at 350℃. The residual ammonia on the char surface was removed using a flow of 50-mL/min N2 gas for 1 h. The char activated this manner is referred to in this paper as PCA.

    PCK was also ammonia-treated in the same manner. The resulting double-activated char is referred to in this paper as PCK + PCA.

       2.2. Characterization of the char

    Nitrogen adsorption/desorption of the char samples pretreated in a vacuum at 200℃ was measured at 77 K using a Sorptomatic (Thermo Fisher Scientific, Waltham, MA, USA). The specific surface area and total pore volume of the char was determined from the adsorption-desorption isotherms using the Brunauer-Emmett-Teller method [56].

    The metal species contained in the char samples were analyzed by inductively coupled plasma atomic emission spectroscopy (ICP-AES, Optima-4300; Perkin Elmer, Waltham, MA, USA).

    X-ray photoelectron spectroscopy (XPS) was performed using an AXIS-NOVA (Kratos Inc., Kyoto, Japan). A monochromatic Al Kα (1486.6 eV) X-ray source and 40 eV analyzer pass energy were used in ultra-high vacuum (5.2 × 10-9 Torr).

    The thermogravimetric characteristics of the char was examined by thermogravimetric analysis (TGA; Pyris 1 TGA, Perkin Elmer) under a 50-mL/min flow of N2 while the temperature was increased from room temperature to 900℃ at a rate of 30℃/min.

       2.3. Adsorption of formaldehyde

    Adsorption experiments were carried out according to the procedure suggested in previous studies [16,51,55]. A 10-liter aluminum bag was flushed using N2 gas and vacuumed. Formaldehyde (100 ppm) was inserted into the bag together with N2 gas to adjust the formaldehyde concentration to 1 ppm. Subsequently, 0.07 g of activated char was placed in the bag, which was then placed in a temperature-controlled incubator maintained at 30℃. To enhance the gas-char mixing, the sample bag was stirred in a shaking incubator.

    The amount of formaldehyde adsorbed was measured at 0, 10, 40, and 80 min using a formaldehyde analyzer (4000 Series; Woori System, Seoul, Korea).

       2.4. NO removal

    The NO removal experiments were performed using a fixed bed reactor. The reactant gas composition was set to NO 1000 ppm, NH3 1000 ppm, and O2 5%, with the balance being N2 gas. The total gas flow-rate was 100 ml/min. The amount of catalyst used for each experiment was 0.3 g, with a W/F (char sample weight/feed flow) ratio of 3 g·min/l (S.V.≒10,000 h−1). Commercial activated carbon developed for air cleaning and odor removal was purchased (Kaya Activated Carbon Inc., Seoul, Korea) for comparison with the activated char used in this study.

    The reaction temperature was between 50℃ and 300℃ at 50℃intervals. A constant temperature was maintained for 30 min at each temperature. The NOx concentration was determined using a NOx analyzer (42i HL; Thermo Fisher Scientific).

    3. Results and Discussion

       3.1. Characteristics of the P. tenera char

    Fig. 2 shows the TGA/differential thermogravimetric analysis of the dried PC. The char mass began to decrease rapidly at approximately 250℃ and the reduction rate slowed down at approximately 500℃. The pyrolysis reactions took place over the temperature range 250℃–500℃. The mass reduction at approximately 100℃ was attributed to evaporation of moisture. After most of the gas and moisture were removed at about 400℃, the mass of the remaining solid decreased gradually. Therefore, 500℃ was chosen as the pyrolysis temperature at which to produce PC.

    Table 1 lists the specific surface areas and total pore volumes of the kinds of char used in this study. The specific surface area of PC produced at 500℃ was below the detection limit. The steam treatment (PCW) increased the specific surface area to 53 m2/g, whereas the increase in specific surface area by ammonia treatment (PCK) was marginal (0.9 m2/g). The KOH treatment (PCK) led to a huge increase in the specific surface area to 1071 m2/g, which was attributed to the removal of considerable ash content (Table 2), resulting in the opening and development of pores [54,55,57]. When PCK was treated further with ammonia (PCK + PCA), the specific surface area was increased further to 1286 m2/g. The specific surface area increase by treatment with ammonia can be attributed to its etching effects. Mangun et al. [58] reported that the specific surface area increased with increasing duration of ammonia treatment and with temperature.

    Fig. 3 presents the nitrogen sorption isotherms and the corresponding pore volumes of the char. PCW and PCA exhibited type-I isotherms, whereas PCK and PCK + PCA showed type-IV isotherms with an H1-type hysteresis loop. The pore size shown in Fig. 3b indicates the coexistence of micropores and mesopores in PCK and PCK + PCA.

    Table 3 lists the ICP elemental analysis results for metals in the PC. The metallic species originated from inorganic matter in the seawater, and accounted for most of the mass of the ash content of seaweed. Among these, Ca, K, and Mg, in particular, enhance the level of formaldehyde adsorption [59].

    Table 4 presents the XPS results. PCW, PCK, and PCA showed a larger quantity of O than did PC. PCA had a larger quantity of N than did PC due to the ammonia treatment. PCK + PCA also had a larger quantity of N than did PCK for the same reason. Na, Cl, P, and K were removed completely by the KOH treatment (PCK and PCK + PCA), leading to a significantly higher C content [51]. O and N enhanced the adsorption capability of the char by forming oxygen- and nitrogen-containing functional groups, respectively, on the char surface.

    Fig. 4 shows the C1s, O1s, and N1s spectra obtained from XPS analysis of the char. The deconvolution of the XPS spectra enabled the identification and intensity determination of surface functional groups. Fig. 4a presents the C1s spectra. Although the intensity depends on the method of activation, all varieties of the char showed a peak at a binding energy level of 285 eV (±0.5 eV), indicating a C-C bond. Three more peaks were observed in all the samples: C-O, C=O, and COO– peaks appearing at 286 eV (±0.5 eV), 287.9 eV (±0.5 eV), and 288.7 eV (±0.5 eV), respectively [60]. Fig. 4b shows the O1s spectra. All the samples exhibited three common peaks: C=O, C-O, and COO peaks, appearing at 531.3 eV (±0.5 eV), 532.7 eV (±0.5 eV), and 533.6 eV (±0.5 eV), respectively [60]. Fig. 4c shows the N1s spectra. The common peaks were observed at two binding energy levels: pyridine N and C-N peaks appeared at 398.7 eV (±0.5 eV) and 400.7 eV (±0.5 eV), respectively [58].

       3.2. Adsorption of formaldehyde by the P. tenera char

    Fig. 5 presents the results of the formaldehyde adsorption experiments using PC, PCW, PCA, PCK, and PCK + PCA. The adsorption rate was highest during the first 10 min, and decreased gradually thereafter. The adsorption of formaldehyde on PCK and PCK + PCA was apparently complete at 40 min. Although PC had the smallest specific surface area and hence the lowest adsorption capability, it showed a formaldehyde removal rate as high as 40% because it contained O- and N-containing functional groups, and a large quantity of metal species. PCW had a larger specific surface area and a smaller quantity of metal species than PC. XPS showed that steam activation increased the quantity of O-containing functional groups on the char surface, resulting in enhanced formaldehyde adsorption. PCA also showed enhanced formaldehyde adsorption ability compared to PC. The adsorption capability of PCA was superior to that of PCW with a larger specific surface area, which was attributed to the large quantity of N-containing functional groups in PCA (see the XPS analysis results). Lee et al. [55] and Yu et al. [61] reported that ammonia treatment of char and mesoporous carbon nitride (MCN) resulted in an increased number of N-containing functional groups and significantly enhanced formaldehyde adsorption ability. The most effective activation method appeared to be KOH activation: PCK exhibited a higher formaldehyde removal rate than did PC, PCW, and PCA. This was attributed to the huge specific surface area (1071 m2/g) and the O- and N-containing functional groups of PCK.

    PCK + PCA showed the highest adsorption capability because it had the largest specific surface area (1286 m2/g) and twice the number of N-containing functional groups as PCK.

    The PC and PCK + PCA were reused after thermal desorption of formaldehyde. Fig. 6 compares the formaldehyde adsorption capabilities of the fresh and recycled chars. The thermal desorption of formaldehyde was conducted under nitrogen gas at 110℃. The reusability of an adsorbent is one of the most important aspects in the economy of adsorption processes. Both PC and PCK + PCA showed little difference between the adsorption rates of fresh and recycled chars, indicating the excellent reusability of both kinds of char.

    Fig. 7 shows the NO conversions obtained using PC, PCK, and activated carbon at different temperatures. PCK and activated carbon showed typical V-shaped curves. The NO conversion obtained below 150℃–200℃ is generally attributed to adsorption and that obtained at higher temperatures is due to the catalytic removal of NOx [62]. PC showed little NO reduction regardless of the temperature. KOH-treated PCK showed approximately 80% NO adsorption at 50℃, which was even higher than that of commercial activated carbon. The high NO removal capability of PCK was attributed to its large specific surface area and O- and N-containing functional groups. In particular, it showed superior ability for NO reduction compared to commercial activated carbon, highlighting the potential for PCK to be commercialized as an alternative NO-adsorbing material. A more detailed comparison versus activated carbon will be carried out in a future study.

    4. Conclusions

    Biochar derived from a seaweed species, Pyropia tenera, was applied to the adsorption of air pollutants. The seaweed char was activated using steam, KOH, and ammonia to improve its adsorption capability. Steam-treatment increased significantly the number of O-containing functional groups on the char surface, whereas the ammonia-treatment increased the number of N-containing functional groups considerably. On the other hand, the KOH-treatment resulted in a huge increase in the specific surface area of the char. Although all the activation methods led to the enhanced formaldehyde adsorption ability of the char, the KOH-treatment appeared to be the best activation method. The activated char produced by the combination of ammonia- and KOH-treatments showed the highest formaldehyde adsorption performance. The KOH-treated char also showed a higher NO reduction capability than did activated carbon.

  • 1. Go JY, Lee S (2012) An appraisal of the urban scheme for sustainable urban transport [Int J Urban Sci] Vol.16 P.261 google doi
  • 2. Kumar A, Pandey AC (2013) Spatio-temporal assessment of urban environmental conditions in Ranchi Township, India using remote sensing and Geographical Information System techniques [Int J Urban Sci] Vol.17 P.117 google doi
  • 3. Kumarage AS, Weerawardana J (2013) System cost-based multicriteria analysis for urban transport solutions [Int J Urban Sci] Vol.17 P.212 google doi
  • 4. Sajjad H, Iqbal M (2012) Impact of urbanization on land use/land cover of Dudhganga watershed of Kashmir Valley, India [Int J Urban Sci] Vol.16 P.321 google doi
  • 5. Park D, Kim NS, Park H, Kim K (2012) Estimating trade-off among logistics cost, CO2 and time: a case study of container transportation systems in Korea [Int J Urban Sci] Vol.16 P.85 google doi
  • 6. Lee JY, Han MY, Kim H (2011) Study on the reduction of pollutant load from roads using the modified hydrodynamic vortex filtration system (HVFS) [Int J Urban Sci] Vol.15 P.35 google doi
  • 7. Lee JY, Han M (2012) Iron removal using adsorptive filtration treatment for low iron concentration water from urban industrial region [Int J Urban Sci] Vol.16 P.115 google doi
  • 8. Wang Y, Hayashi Y, Kato H, Liu C (2011) Decomposition analysis of CO2 emissions increase from the passenger transport sector in Shanghai, China [Int J Urban Sci] Vol.15 P.121 google doi
  • 9. Lee SB, Shin MK, Hong IK (2011) Phase behavior of Sick House Syndrome (SHS) chemicals [J Ind Eng Chem] Vol.17 P.554 google doi
  • 10. Kim DI, Park JH, Kim SD, Lee JY, Yim JH, Jeon JK, Park SH, Park YK (2011) Comparison of removal ability of indoor formaldehyde over different materials functionalized with various amine groups [J Ind Eng Chem] Vol.17 P.1 google doi
  • 11. Tian F, Wu Z, Yan Y, Ge X, Tong Y (2015) Photodegradation of formaldehyde by activated carbon loading TiO2 synthesized via microwave irradiation [Korean J Chem Eng] Vol.32 P.1333 google doi
  • 12. Khanmohammadi M, Garmarudi AB, Elmizadeh H, Roochi MB (2014) Spectrophotometric evaluation of the photocatalytic degradation of formaldehyde by Fe2O3?TiO2 nano hybrid [J Ind Eng Chem] Vol.20 P.1841 google doi
  • 13. Jeon SW, Lee JE, Park JK, Kim SH (2015) Oxidation of formaldehyde, carbon monoxide and methanol over manganesecerium-aluminum oxides supported on cordierite monoliths [Korean J Chem Eng] Vol.32 P.230 google doi
  • 14. Xu Z, Hou H (2010) Formaldehyde removal from air by a biodegradation system [Bull Environ Contam Toxicol] Vol.85 P.28 google doi
  • 15. Ahmed F, Cho HJ, Kim JK, Seon NU, Yeo YK (2015) A real-time model based on least squares support vector machines and output bias update for the prediction of NOx emission from coal-fired power plant [Korean J Chem Eng] Vol.32 P.1029 google doi
  • 16. Ko JH, Park R, Jeon JK, Kim DH, Jung SC, Kim SC, Park YK (2015) Effect of surfactant, HCl and NH3 treatments on the regeneration of waste activated carbon used in selective catalytic reduction unit [J Ind Eng Chem] Vol.32 P.109 google doi
  • 17. Luo X, Zhang Z, Zhou P, Liu Y, Ma G, Lei Z (2015) Synergic adsorption of acid blue 80 and heavy metal ions (Cu2+/Ni2+) onto activated carbon and its mechanisms [J Ind Eng Chem] Vol.27 P.164 google doi
  • 18. Hajati S, Ghaedi M, Yaghoubi S (2015) Local, cheep and nontoxic activated carbon as efficient adsorbent for the simultaneous removal of cadmium ions and malachite green: optimization by surface response methodology [J Ind Eng Chem] Vol.21 P.760 google doi
  • 19. Asadullah M, Jahan I, Ahmed MB, Adawiyah P, Malek NH, Rahman MS (2014) Preparation of microporous activated carbon and its modification for arsenic removal from water [J Ind Eng Chem] Vol.20 P.887 google doi
  • 20. Ghaedi M, Ansari A, Habibi MH, Asghari AR (2014) Removal of malachite green from aqueous solution by zinc oxide nanoparticle loaded on activated carbon: kinetics and isotherm study [J Ind Eng Chem] Vol.20 P.17 google doi
  • 21. Guo Q, Jing W, Cheng S, Huang Z, Sun D, Hou Y, Han X (2015) Promoting role of sulfur groups in selective catalytic reduction of NO with NH3 over H2SO4 modified activated carbons [Korean J Chem Eng] Vol.32 P.2257 google doi
  • 22. Daoud W, Ebadi T, Fahimifar A (2015) Optimization of hexavalent chromium removal from aqueous solution using acid-modified granular activated carbon as adsorbent through response surface methodology [Korean J Chem Eng] Vol.32 P.1119 google doi
  • 23. Xiao X, Tian F, Yan Y, Wu Z, Wu Z, Cravotto G (2015) Adsorption behavior of phenanthrene onto coal-based activated carbon prepared by microwave activation [Korean J Chem Eng] Vol.32 P.1129 google doi
  • 24. Alhamed YA, Rather SU, El-Shazly AH, Zaman SF, Daous MA, Al-Zahrani AA (2015) Preparation of activated carbon from fly ash and its application for CO2 capture [Korean J Chem Eng] Vol.32 P.723 google doi
  • 25. Dai W, Yu H, Ma N, Yan X (2015) Adsorption equilibrium and kinetic studies of crystal violet and naphthol green on torreya-grandis-skin-based activated carbon [Korean J Chem Eng] Vol.32 P.335 google doi
  • 26. Bandosz TJ (2002) On the adsorption/oxidation of hydrogen sulfide on activated carbons at ambient temperatures [J Colloid Interface Sci] Vol.246 P.1 google doi
  • 27. Mubarik S, Saeed A, Athar MM, Iqbal M (2016) Characterization and mechanism of the adsorptive removal of 2,4,6-trichlorophenol by biochar prepared from sugarcane baggase [J Ind Eng Chem] Vol.33 P.115 google doi
  • 28. Ding Z, Hu X, Wan Y, Wang S, Gao B (2016) Removal of lead, copper, cadmium, zinc, and nickel from aqueous solutions by alkali-modified biochar: batch and column tests [J Ind Eng Chem] Vol.33 P.239 google doi
  • 29. Low LW, Teng TT, Alkarkhi AFM, Morad N, Azahari B (2015) Carbonization of Elaeis guineensis frond fiber: effect of heating rate and nitrogen gas flow rate for adsorbent properties enhancement [J Ind Eng Chem] Vol.28 P.37 google doi
  • 30. Abdel-Fattah TM, Mahmoud ME, Ahmed SB, Huff MD, Lee JW, Kumar S (2015) Biochar from woody biomass for removing metal contaminants and carbon sequestration [J Ind Eng Chem] Vol.22 P.103 google doi
  • 31. Maneechakr P, Samerjit J, Uppakarnrod S, Karnjanakom S (2015) Experimental design and kinetic study of ultrasonic assisted transesterification of waste cooking oil over sulfonated carbon catalyst derived from cyclodextrin [J Ind Eng Chem] Vol.32 P.128 google doi
  • 32. Anirudhan TS, Shainy F (2015) Adsorption behaviour of 2-mercaptobenzamide modified itaconic acid-grafted-magnetite nanocellulose composite for cadmium(II) from aqueous solutions [J Ind Eng Chem] Vol.32 P.157 google doi
  • 33. Liu QY, Yang F, Liu ZH, Li G (2015) Preparation of SnO2?Co3O4/C biochar catalyst as a Lewis acid for corncob hydrolysis into furfural in water medium [J Ind Eng Chem] Vol.26 P.46 google doi
  • 34. Elaigwu SE, Rocher V, Kyriakou G, Greenway GM (2014) Removal of Pb2+ and Cd2+ from aqueous solution using chars from pyrolysis and microwave-assisted hydrothermal carbonization of Prosopis africana shell [J Ind Eng Chem] Vol.20 P.3467 google doi
  • 35. Yang J, Yu M, Chen W (2015) Adsorption of hexavalent chromium from aqueous solution by activated carbon prepared from longan seed: kinetics, equilibrium and thermodynamics [J Ind Eng Chem] Vol.21 P.414 google doi
  • 36. Mohammadi SZ, Hamidian H, Moeinadini Z (2014) High surface area-activated carbon from Glycyrrhiza glabra residue by ZnCl2 activation for removal of Pb(II) and Ni(II) from water samples [J Ind Eng Chem] Vol.20 P.4112 google doi
  • 37. Ghasemi M, Naushad M, Ghasemi N, Khosravi-fard Y (2014) Adsorption of Pb(II) from aqueous solution using new adsorbents prepared from agricultural waste: adsorption isotherm and kinetic studies [J Ind Eng Chem] Vol.20 P.2193 google doi
  • 38. Ghasemi M, Naushad M, Ghasemi N, Khosravi-fard Y (2014) A novel agricultural waste based adsorbent for the removal of Pb(II) from aqueous solution: kinetics, equilibrium and thermodynamic studies [J Ind Eng Chem] Vol.20 P.454 google doi
  • 39. Ruthiraan M, Mubarak NM, Thines RK, Abdullah EC, Sahu JN, Jayakumar NS, Ganesan P (2015) Comparative kinetic study of functionalized carbon nanotubes and magnetic biochar for removal of Cd2+ ions from wastewater [Korean J Chem Eng] Vol.32 P.446 google doi
  • 40. Lingamdinne LP, Roh H, Choi YL, Koduru JR, Yang JK, Chang YY (2015) Influencing factors on sorption of TNT and RDX using rice husk biochar [J Ind Eng Chem] Vol.32 P.178 google doi
  • 41. Hashemian S, Salari K, Yazdi ZA (2014) Preparation of activated carbon from agricultural wastes (almond shell and orange peel) for adsorption of 2-pic from aqueous solution [J Ind Eng Chem] Vol.20 P.1892 google doi
  • 42. Zhang Z, Feng X, Yue XX, An FQ, Zhou WX, Gao JF, Hu TP, Wei CC (2015) Effective adsorption of phenols using nitrogen-containing porous activated carbon prepared from sunflower plates [Korean J Chem Eng] Vol.32 P.1564 google doi
  • 43. Nizamuddin S, Jayakumar NS, Sahu JN, Ganesan P, Bhutto AW, Mubarak NM (2015) Hydrothermal carbonization of oil palm shell [Korean J Chem Eng] Vol.32 P.1789 google doi
  • 44. Zwieten LV, Kimber S, Morris S, Chan KY, Downie A, Rust J, Joseph S, Cowie A (2010) Effects of biochar from slow pyrolysis of papermill waste on agronomic performance and soil fertility [Plant Soil] Vol.327 P.235 google doi
  • 45. Atkinson CJ, Fitzgerald JD, Hipps NA (2010) Potential mechanisms for achieving agricultural benefits from biochar application to temperate soils: a review [Plant Soil] Vol.337 P.1 google doi
  • 46. Cho HJ, Baek K, Jeon JK, Park SH, Suh DJ, Park YK (2013) Removal characteristics of copper by marine macro-algae-derived chars [Chem Eng J] Vol.217 P.205 google doi
  • 47. Bae YJ, Ryu C, Jeon JK, Park J, Suh DJ, Suh YW, Chang D, Park YK (2011) The characteristics of bio-oil produced from the pyrolysis of three marine macroalgae [Bioresour Technol] Vol.102 P.3512 google doi
  • 48. Wang S, Jiang XM, Wang N, Yu LJ, Li Z, He PM (2007) Research on pyrolysis characteristics of seaweed [Energy Fuels] Vol.21 P.3723 google doi
  • 49. Figueira MM, Volesky B, Ciminelli VST, Roddick FA (2000) Biosorption of metals in brown seaweed biomass [Water Res] Vol.34 P.196 google doi
  • 50. Yun YS, Park D, Park JM, Volesky B (2001) Biosorption of trivalent chromium on the brown seaweed biomass [Environ Sci Technol] Vol.35 P.4353 google doi
  • 51. Kim BS, Lee HW, Park SH, Baek K, Jeon JK, Cho HJ, Jung SC, Kim CS, Park YK (2015) Removal of Cu2+ by biochars derived from green macroalgae [Environ Sci Pollut Res] Vol.23 P.985 google doi
  • 52. Park SH, Cho HJ, Ryu C, Park YK (2016) Removal of copper(II) in aqueous solution using pyrolytic biochars derived from red macroalga Porphyra tenera [J Ind Eng Chem] Vol.36 P.314 google doi
  • 53. Cha JS, Park SH, Jung SC, Ryu C, Jeon JK, Shin MC, Park YK Production and utilization of biochar: a review [J Ind Eng Chem] google doi
  • 54. Park MS, Cho S, Jeong E, Lee YS (2015) Physico-chemical and electrochemical properties of pitch-based high crystallinity cokes used as electrode material for electric double layer capacitor [J Ind Eng Chem] Vol.23 P.27 google doi
  • 55. Lee JY, Park SH, Jeon JK, Yoo KS, Kim SS, Park YK (2011) The removal of low concentration formaldehyde over sewage sludge char treated using various methods [Korean J Chem Eng] Vol.28 P.1556 google doi
  • 56. Lee EH, Park RS, Kim H, Park SH, Jung SC, Jeon JK, Kim SC, Park YK (2016) Hydrodeoxygenation of guaiacol over Pt loaded zeolitic materials [J Ind Eng Chem] Vol.37 P.18 google doi
  • 57. Fierro V, Muniz G, Basta AH, El-Saied H, Celzard A (2010) Rice straw as precursor of activated carbons: activation with ortho-phosphoric acid [J Hazard Mater] Vol.181 P.27 google doi
  • 58. Mangun CL, Menak KR, Economy J, Foster KL (2001) Surface chemistry, pore sizes and adsorption properties of activated carbon fibers and precursors treated with ammonia [Carbon] Vol.39 P.1809 google doi
  • 59. Busca G, Lamotte J, Lavalley JC, Lorenzelli V (1987) FT-IR study of the adsorption and transformation of formaldehyde on oxide surfaces [J Am Chem Soc] Vol.109 P.5197 google doi
  • 60. Murphy V, Tofail SAM, Hughes H, McLoughlin P (2009) A novel study of hexavalent chromium detoxification by selected seaweed species using SEM-EDX and XPS analysis [Chem Eng J] Vol.148 P.425 google doi
  • 61. Yu MJ, Vinu A, Park SH, Jeon JK, Jhung SH, Park YK (2014) Application of MCN-1 to the adsorptive removal of indoor formaldehyde [Sci Adv Mater] Vol.6 P.1511 google doi
  • 62. Cha JS, Choi JC, Ko JH, Park YK, Park SH, Jeong KE, Kim SS, Jeon JK (2010) The low-temperature SCR of NO over rice straw and sewage sludge derived char [Chem Eng J] Vol.156 P.321 google doi
  • [Fig. 1.] Schematic diagram of seaweed pyrolysis apparatus.
    Schematic diagram of seaweed pyrolysis apparatus.
  • [Fig. 2.] Thermogravimetric analysis (TGA)/differential thermogravimetric of dried Pyropia tenera.
    Thermogravimetric analysis (TGA)/differential thermogravimetric of dried Pyropia tenera.
  • [Table 1.] Physical properties of Pyropia tenera char
    Physical properties of Pyropia tenera char
  • [Table 2.] Ash content in the kinds of char
    Ash content in the kinds of char
  • [Fig. 3.] Nitrogen sorption isotherms (a) and the corresponding pore volume (b). PC, Pyropia tenera char; PCA, ammonia activated PC; PCW, steam activated PC; PCK, KOH activated PC.
    Nitrogen sorption isotherms (a) and the corresponding pore volume (b). PC, Pyropia tenera char; PCA, ammonia activated PC; PCW, steam activated PC; PCK, KOH activated PC.
  • [Table 3.] Elemental analysis of Pyropia tenera char
    Elemental analysis of Pyropia tenera char
  • [Table 4.] Elemental surface composition of Pyropia tenera char
    Elemental surface composition of Pyropia tenera char
  • [Fig. 4.] X-ray photoelectron spectroscopy spectra of Pyropia tenera samples: (a) Spectrum at C1s (b) Spectrum at O1s (c) spectrum at N1s. PC, Pyropia tenera char; PCW, steam activated PC; PCA, ammonia activated PC; PCK, KOH activated PC.
    X-ray photoelectron spectroscopy spectra of Pyropia tenera samples: (a) Spectrum at C1s (b) Spectrum at O1s (c) spectrum at N1s. PC, Pyropia tenera char; PCW, steam activated PC; PCA, ammonia activated PC; PCK, KOH activated PC.
  • [Fig. 5.] Adsorption of formaldehyde over Pyropia tenera char treated using various methods. PC, Pyropia tenera char; PCW, steam activated PC; PCA, ammonia activated PC; PCK, KOH activated PC.
    Adsorption of formaldehyde over Pyropia tenera char treated using various methods. PC, Pyropia tenera char; PCW, steam activated PC; PCA, ammonia activated PC; PCK, KOH activated PC.
  • [Fig. 6.] Adsorption and desorption of formaldehyde over Pyropia tenera char. PC, PC, Pyropia tenera char; PCK, KOH activated PC; PCA, ammonia activated PC.
    Adsorption and desorption of formaldehyde over Pyropia tenera char. PC, PC, Pyropia tenera char; PCK, KOH activated PC; PCA, ammonia activated PC.
  • [Fig. 7.] NO conversion of char and activated carbon. PC, Pyropia tenera char; PCK, KOH activated PC.
    NO conversion of char and activated carbon. PC, Pyropia tenera char; PCK, KOH activated PC.